Demands good wear resistance with better caliber surface, materials used can range from conventional to special grades depending on the rolling conditions and rolling requirements.
CONVENTIONAL GRADES
SG PEARLITIC
SG Pearlitic is characterised by nodular graphite and carbides arranged in a pearlitic matrix. Its properties are similar to Alloy Indefinite Chill except the graphite structure is changed from flake shapes to spheroidal forms. SG Pearlitic rolls will have higher strength than Indefinite Chill. SG Pearlitic rolls are suitable both roughing and finishing, and a wide range of applications. This grade can be produced by Static casting (Monoblock) or using the Centrifugal Cast (CC) Double pour method. In addition various SG Pearlitic grades have been introduced:
SGP grades alloyed with Chromium to achieve a deep penetration of carbides. These grades have a lower hardness drop and good wear resistance properties and is recommended for rolls with deep grooves.
SGP grades alloyed with Molybdenum and Nickel subjected to high temperature heat treatment have an excellent resistance to fire cracking properties along with high strength. The impact resistance is also increased over that of flake graphite iron.
SPECIFICATIONS
Production Type Static Monobloc or Centrifugal Cast Double Pour Materials
Chemical C 3.00-3.40 | Si 1.00-2.00 | Mn 0.30-0.80 | Ni 1.00-2.60 | Cr 0.10-0.90 | Mo 0.30-0.80
Hardness 40-65 HSc | Tensile ≥ 400-600 Mpa | Bending ≥ 600-900 Mpa
SG ACICULAR
SG Acicular, alloyed with the Nickel, Manganese and Chromium with a Bainitic-Acicular-Martensitic matrix has a higher UTS, hardness and is more wear resistant than the SG Pearlitic quality. Semi- continuous carbides maintain the wear resistance while at the same time exhibiting high strength and resistance to firecracks. Extensive heat treatment procedure ensures an acicular matrix. This grade can be produced by Static casting (Monoblock) or using the Centrifugal Cast (CC) Double pour method.
SG Acicular grades alloyed with Chromium to achieve a deep penetration of carbides. These grades have a lower hardness drop, better wear resistance properties, and is recommended for rolls with deep grooves.
SPECIFICATIONS
Production Type Static Monobloc or Centrifugal Cast Double Pour Materials
Chemical C 3.00-3.50 | Si 1.00-2.20 | Mn 0.30-1.00 | Ni 2.50-5.00 | Cr 0.30-1.50 | Mo 0.30-1.00
Hardness 61-78 HSc | Tensile ≥ 400-500 Mpa | Bending ≥ 600-750 Mpa
ALLOY INDEFINITE CHILL
Alloy Indefinite Chill rolls consist of cast iron with fine interdendritic graphite evenly dispersed throughout the barrel of the roll. The size, shape and distribution of the graphite together with the carbide content is controlled by the chilling effect and the alloy content. The addition of alloys such as manganese, nickel, chromium, and molybdenum changes the matrix structure from pearlitic, through bainite, to martensitic. The carbide form is altered from semi-continuous to rigid continuity enhancing the strength, hardness in depth and wear resistance properties.
The fine graphite enhances the resistance to the thermal stresses by increasing the thermal conductivity, thus reducing fire cracks. Its increased shock resistance (damping capacity) helps to reduce spalling particularly when large reductions in section are required.
The gradual change in hardness makes it ideal for deeper grooving and can be used in both roughing and finishing stands for bar and sections, and for roughing and intermediate stands of wire and rod mills. AIC rolls with artensitic structure and high hardness are suitable for finishing stands of wire mills. This grade can be produced by Static casting (Monoblock) or using the Centrifugal Cast (CC) Double pour method.
SPECIFICATIONS
Production Type Static Monobloc or Centrifugal Cast Double Pour Materials
Chemical C 3.00-3.50 | Si 0.60-1.20 | Mn 0.50-1.20 | Ni 1.00-5.00 | Cr 0.70-2.00 | Mo 0.10-0.50
Hardness 51-85 HSc | Tensile ≥ 380-500 Mpa | Bending ≥ 580-700 Mpa
SPECIAL GRADES
RÁPIDO HSS
RÁPIDO HSS rolls have high hardness and good wear resistance at high temperatures. This grade is only produced by the horizontal Centrifugal Cast (CC) method and has the core material in spheroidal graphite pearlitic iron. The composition and subsequent heat treatment ensures the hardness of the working layer of the HSS material will reach 80/85° shore ‘C’, with uniform hardness throughout the working layer, while the structure of complex carbides of Vanadium, Tungsten, Niobium and Molybdenum in a martensitic matrix ensures uniform wear as well as high wear resistance. This type of roll is used in finishing applications for increased campaign times and better surface finish.
SPECIFICATIONS
Production Type Centrifugal Cast Double Pour Materials
Chemical C 1.6-2.0 | Si 0.3-1.0 | Mn 0.3-1.0 | Cr 4.0-8.0 | Mo 4.0-6.0 | Cr 4.0-6.0 | Ni 0.5-1.5
Hardness 70-85 HSc | Tensile ≥ 700-900 Mpa | Bending ≥ 700-1100 Mpa
RÁPIDO TOOLSTEEL
Demand for new alternatives for tungsten carbide have led to the development of an iron-matrix material with increasing carbide contents. We are introducing RÁPIDO TOOLSTEEL which can be used in highest and lowest rolling speed. This can be used in rolling mills for pinching, looping and transporting, KOCKS reduction and Sizing Block, Composite Rolls in Pre-finishing stands.
SPECIFICATIONS
Production Type Sintered Materials
Chemical C ** | Si ** | Mn ** | P 0.03 | S 0.03 | V 3.7-4.5 | Cr 0.45-1.20 | W 5.2-6.5
Hardness 35-50 HSc
TUNGSTEN CARBIDE
SPECIFICATION
Production Type Sintered Materials
Chemical W 8-32% | CoNiCr 68-92%
Hardness 35-50 Hra